Leader Clipperlon 2100

Contact

Ask Leader Gasket

Do you have a question? Feel free to contact us!

Description

Modified PTFE sheet manufactured with biaxial oriented longer molecule chains specially designed for high demanding applications. Due to this specific material structure and special manufacturing process a low creep properties are achieved. Fawn in color and produced with Modified PTFE and Solid Silica Beads as a filler.

Available also for Heat Exchanger applications.

Downloads

Product Data Sheet

Application

A general purpose gasket material for sealing applications across the whole pH-range, reduced creep, and good sealability at low stress.

Advtantages

Clipperlon 2100 has a very good cold flow resistance and good stress retention properties, even at elevated termperatures. Because of the low diffusion properties and uniform structure, Clipperlon 2100 is the ideal sealing material for applications with the highest demands for low emissions.

Chemical Compatiblity

Particularly suitable for use with strong acids (except hydrofluoric acid) and alkalis. Other applications include solvents, fuels, water, steam and chlorine. A chemical resistance list available upon request. Pressure up to 1200 psi. Temperature from -450 °F up to 500 °F.

Delivery Options

Flange gaskets and sheets are available in thickness of 1/32",1/16", 1/8". Other thicknesses available on request. Standard gaskets can be supplied in accordance with ASME B16.21. Non-standard or special gaskets can be manufactured according to customer drawings, or by given sizes or Edrawing.

Temperature

Approvals & Certificates

FDA 21 CFR 177.1550
TA-Luft
EC1935 (10/2011)
TA-Luft
FDA 21 CFR 177.1550
EC1935 (10/2011)

Sealing Characteristics

significant reduced creep
low leak rate
good electrical insulation properties
outstanding chemical resistance
Non-ageing
excellent sealability

Technical Data
max Temperature [°F]	500
max Temperature [°C]	260
max Pressure [psi]	1200
density [g/cm3]	2.2
Leakage Specific Leak Rate [DIN 28090-2] [mg/(s*m)]	0.01
Minimum initial stress [DIN E 2505 part 2] [N/mm2]	20
Maximum initial stress [DIN E 2505 part 2] [N/mm2]	200
M-Value	3.5
Y- Value [psi]	2450
min Seating stress [Qmin(L 0,01), mg/(s*m)] at RT 40 bar [N/mm2]	31
ASTM F36 Recovery [% min]	40
Gasket required flange roughness [Ra micron]	3,2-6,3
Gasket required flange roughness [RMS]	125-250
max Seating stress [Qsmax bei RT EN13555] [n/mm2]	200
Tensile Strength (quer) DIN 52910 [N/mm²]	>= (13) 1885
Advice Seating stress at assembly [psi]	5000
ROTT [Gb]	495
ROTT [a]	0.301
ROTT [Gs"]	5.87
compressability, [ASTM F36], [%]	7-10
ASTM F36 Recovery [% min]	40
ASTM F37 Sealability [ml/min] Sg=1000 psi=30	0.01
ASTM F38 Creep Relaxation [%]	15
ASTM F152 Average Tensile [psi]	2000

Clipperlon 600

Leader Clipperlon 600 Joint Sealant is made from 100% pure monodirectional expanded PTFE. FDA and EC1935-10/2011 approved...

Clipperlon 660

Leader Clipperlon 660 is the new generation of multidirectionally expanded PTFE gasket tapes for use inpipeline and apparatus flanges. FDA and EC1935-10/2011 approved...

Leader Clipperlon 2110

Biaxially oriented PTFE sheet that contains hollow glass microespheres as filler.Color : Blue...

Leader Clipperlon 2115 USP

Modified PTFE(bi-axial) sheet, white in color (no pigment) and produced with Modified PTFE and hollow glass microspheres as a filler. Suitable for low torque applications, plastic pipe systems and flanges, as well as glass and cer...